How To Stack Welds In 2F Position
Vložit
- čas přidán 4. 11. 2021
- Having trouble stacking beads correctly in your 2F horizontal welds? This video shows tried and true tricks on how to correctly stack your beads for a fillet weld with even legs.
- Jak na to + styl
in my opinion this is the best fillet weld instruction video on You Tube. Very clear instructions. I started to make beautiful welds after fallowing this instruction. Before I just could not make it even. Thank You!
I agree
The video is quite detailed, its the first video am watching on this channel too! Must say i was the disappointed
Facts
I’m so glad I could help!
Amazing video and instructions, thank you for this, you’re a great teacher! I haven’t had anyone explain something so easy to understand before and so thoroughly.
Einstein quote: “If you can't explain it simply, you don't understand it well enough.”
Very much appreciated this video! Hope to learn more from you in the future! 🫡👏🏽
Seen most of if not all CZcams 2F videos. This is a very well made video that meticulously explains the process. The visual aid highlights and rod angles are perfection.
Thank you! I’m glad you liked it.
phenomenal video, I would love to see your explanation and advice for 3F-up/down and 4F this video explained things so clearly
Thank you! I’m filming 3F this week.
the video editing really helps. most vids talking about the technique, only talk about it
man this helped me alot i've had problems stacking beads now i know its the way i hold the angle
Thank you SO much!!! This video transformed me into a PRO in one day! If you put in the work, you will get there
So glad my video helped you out so much! I’ll be putting more up soon.
exellent cant ask for a better video
This video is super helpful. I wish you made more, like how to stack welds in a 4F position.
Awesome video, man. I struggle with this a lot but I’m getting better and this video really helped
So glad I could help!
Great video, straight to the point. Helped me a lot, thank you!
Im glad I could help!
Thanks for the advice
I love welding, its an awesome skill and my hat off for fellow welders!
This is video is amazing. Thank you!!
Excellent welds and examples.
Thank you so much. Very clear and detailled explanations 👍. Helped me so much👏
You’re welcome! I’m glad it helped.
Very well put together thank you this is going to help me alot in my welding class thank you
Thank you! I’ll have more videos up soon to help with the other joints
Great vidoe!. Wedling H joints with a 6010 at the moment in school. This helps thnks.
Literally better then the videos with thousand of views . Keep up the good work
Thank you! That’s very kind of you
Thank you so much👍👍
Amazing video!
Thanks, finally I could find a video I was looking for
Thank you for this video! Very helpful. Please post more videos. Blessings
Happy to hear it helped you. I’ll have more coming soon.
Broooo you only have one video you should do more. I’m welding at a technical college and your video helped a lot. I showed the video to my classmates and it helped them as well. Please make🙏🏽🙏🏽
Glad it helped so much! I’ll have more coming soon.
Nice explanation.....keep going 💪
💗💗Brother I saw your video from Bangladesh. I enjoyed watching your video. Thanks brother. I wish you a healthy life to God.💓💓
Thank you!
Very Helpful 💯
Glad I could help!
thanks. I hope you also do a 3f stacking. Waiting here👋
Thanks!
Greetings from Spain. I’ll try to do it with mig mag machine. I’m struggling to do it as well.
Good man
খুবেই ভালো লাগলো।🇧🇩
❤🎉🎉🎉😊 gracias
❤
Great video! Will you be making anymore?
Thank you! I have a video on 3F 7018 coming soon.
Can you do one for mig pulse? Im confused on the angles with that process. The top bead is hard for me undercut is an issue
how about vertical position layering do you have a video.? thanks
Can you upload more videos please 😊
What happened you didn’t post more videos?
how do you know how many stacks are required on the fillet weld? like how the total size of the final result?
I'm currently doing this in school using a 6010 rod. But they want us to do whips (back and forth motion) and circles.
That makes sense with it being a fast freeze rod. The technique shown for stacking the beads would still apply.
I have to do this in 3f and I can't cover the previous pass enough the whole way. I start to go off to the left or right.
Same position,but your vertical plate had a radius. Not sure how take stack without slag in trapement
Do you adjust your amperage as you build beads or does it stay the same throughout the entire process
Great question, amperage should stay the same throughout, I have seen some instructors recommend going hotter on the last (6) weld however it’s more of a preference, I know when I am running 1/8 7018 I stay at 119 for all passes, other guy I know will run 110 then on the very last weld bump it to 118 and his come out just the same as mine
Either let it cool down between passes or cut the amperage down a little each pass for the last couple. Helps a lot.
How do you get a 3/32 to last for an entire pass? Mine always burn 2-4 per pass and if I try to speed up, it underfills
Amperage, if you are running the same speed as in the video consistently you should have the rod to the stinger at the end, it’s definitely speed and amperage, you may be running a little too hot, and by underfills do you mean undercut or cold lap?
Please do 3F
Planning on doing 3F this week.
They should show this to people in welding school because you move from 7018 overhead on 3/4 to fillet welds on metal half that thickness. I picked up on it pretty quick but some but just get lost in it.