Abe wants to let us know the secrets for getting gold on your stainless steel caps. He will use the tig welding process on a Everlast Powertig 250EX. #stainless #steel #tigwelding
I think he had the order of color wrong, it starts shiny silver then gold, then straw, then blue and purple... I think he welded that first pass on the edge so the heat had nowhere to go... he let it cool and his 2nd pass picked up oxides from the first weld, thats why it was blue on that side... but I gotta give it to him, some excellent techniques 👏👍
That's how I thought it worked but why didn't it go back to blue at any point after the gold welds if that is how it works? It just transitioned into red colors as it got hotter.
Hey Abraham I’m an X-ray tech and I worked a long time around your dad in Tomball. Just checking up on him to see how y’all are doing since he got laid off. Your dad is a very very very good welder! Tell him I said “Todo Bueno”!! Lol he knows
@@abrahamjasmine thanks for replying. I got much love for your dad! He is a good dude! He always went out of his way to come say hello to me no matter what. Ask him who is the (todo bueno thumbs up 👍 guy) lol
I've never struck an arc with a tig rig but weldtube gives me the confidence to try. Everlast Christmas present to myself coming soon. New angles, new opportunities, new money.
The sch 80 pipe is cheating a little.. But the color is affected by cleanliness, temp amps/travel, gas coverage wide and low is better than narrow and fast, and the filler metal.. some alloy filler metal are just crap.. you can keep the same setting, change filler and get different results..
Great video but the fact that your on XS pipe and larger bore helps tremendously with color… we need one of how to maintain proper color on 2 ,3,4 inch school 10 stainless lol that’s where the lord’s work is done… 🙏
I’ve actually been having problems welding lately. On my most recent job I’ve been doing mostly stainless, schedule 10, and a lot of small diameter. I suppose it’s important that I mention I am still fairly new in the field. I tend to get deep reds in my welds which tells me I’m very near burning the stainless up. The problem is, sometimes I get it even when I strike up on a cold pipe. My coworkers say it’s because my tungsten isn’t out far enough and I’m moving too slow. Do you have any thoughts or anything to add to the reasons I’m getting these colors?
I recently work with stainless stell pipe, mostly thin pipe like sch 20 to sch 40, when doing welding on flange the color is show up but when welding on the pipe joint there is no color, jist dark grey, still figured it out why
Believe it or not I worked for ETS in a fab shop all stainless and exotic metals, never touched a tig rig, I was a helper then slowly learned how to tack, then I was a tacker then learned how to throw a root in stainless and kept moving forward and now I struggle to learn stick, I can throw a root w 6010 but it ain’t all that slick, detailed tutorial? Root-Cap 6010/7018 ?
The way you angle you’re rod , whipping pattern being consistent and amps when I was in high school my teacher told me to whip it and hold In the puddle for one second then go out , keep you’re eyes at the weld I had the bad habit of watching the rod leave then would loose my straight line
Nice consistency man you got that golden arm! I'm practicing on plate right now, in that frustrating learning phase, many many hours to go. Eventually it'll click hopefully! Your guys tips have been very helpful
@@mrillis9259 It's like riding a bicycle, when you get that motion down it's all muscle memory. Unfortunately I went Aerospace and there is no walking the cup due to the scratching of base material.
how is it you are getting less and less heat affected welds when welding over the same hot area? i wish someone could teach me how to walk the dog to get these welds, i have a test for 3" nom 304 pipe with a 1/16 gap but my weld was greyish and not good , idk if it was the metal or im just not good standing and trying to weld this out of position as i said perhaps if i knew the dog trick it would be a better weld
Important info to understand what your metal is doing as the heat goes up. Great video and beautiful consistent welds. Are the colour changes evident in all metals when welding or only on stainless steel?
Hello. My name is Sasha. I'm from London. I like your approach to teaching. But you always miss the point. And the main thing is when you need to show the wire feed manually. How to hold the wire in your hands. Position of legs and body. And the most important thing is the manipulation of the hand. And it would be nice to show it all in one video and close-up. I hope that many beginner welders will be grateful to you. Thank you for understanding.
@@kf8575 Thank you; I can see it now. I didn't know about the gold lens. Now that I have tried it, I can also see the colors of the HAZ through my auto lens, although that requires a fine adjustment of shade level, which is hard to guess without testing.
well lets do it on a 1 inch sch 40 stailess steel pipe ,, from 6 o clock to 12 o clock with a regular machine just dc machine out on the field lets go lets say a clasic 300 lincols diesel ????
So grey and purple and blue , are not a favorite color , but do they pass the X-ray Or grey a sign of poor welding besides a ugly non favorite color for a cap ??
It will pass xray, but if it’s burnt to much you will lose nickel content which is what aids in the corrosion resistance of stainless. Which basically defeats the purpose of using stainless to begin with.
Как вариант - от перегрева шва может скользить. А так - есть способ - на лепестковом круге на болгарке поточи немного торец сопла, только на небольшой скорости, скользить перестанет
👇WeldTube Store👇
www.weldlife.com
I think he had the order of color wrong, it starts shiny silver then gold, then straw, then blue and purple... I think he welded that first pass on the edge so the heat had nowhere to go... he let it cool and his 2nd pass picked up oxides from the first weld, thats why it was blue on that side... but I gotta give it to him, some excellent techniques 👏👍
That's how I thought it worked but why didn't it go back to blue at any point after the gold welds if that is how it works? It just transitioned into red colors as it got hotter.
Hey Abraham I’m an X-ray tech and I worked a long time around your dad in Tomball. Just checking up on him to see how y’all are doing since he got laid off. Your dad is a very very very good welder!
Tell him I said “Todo Bueno”!! Lol he knows
I appreciate you bro , I will let home know , and he is good , enjoying that retired lifestyle ! And he is working out
@@abrahamjasmine thanks for replying. I got much love for your dad! He is a good dude!
He always went out of his way to come say hello to me no matter what.
Ask him who is the (todo bueno thumbs up 👍 guy) lol
I've never struck an arc with a tig rig but weldtube gives me the confidence to try. Everlast Christmas present to myself coming soon. New angles, new opportunities, new money.
Great tips man! Can tell you've been welding for many years
High amps, giving high travel speed, gives lower heat input.
Caps coming out dark? Crank the amps and travel speed up👍
How do I step out further with my weave? My weaves are always really tight
@@firecracker4277 torch angle, cup size and stick out of tungsten will all affect it
Also travel speed matters - you go faster and color's gets nicer
Excellent video Abraham!
I am also a welder and love your videos.
Great experiment, respect!
Hey brother, thats some awesome techniques your using, love the quality👍
I just found your channel. You guys are awesome, keep making movie quality videos.
The sch 80 pipe is cheating a little..
But the color is affected by cleanliness, temp amps/travel, gas coverage wide and low is better than narrow and fast, and the filler metal.. some alloy filler metal are just crap.. you can keep the same setting, change filler and get different results..
Man, that’s near perfect!
Awesome finished product man.
I fuckin hate TIG welding stainless. Doing pipe at work for the first time and this kid make it look easy
I love the two views at 5:30, I know I learn more visually and seeing how he moves around the pipe helps.
Can’t wait till I can make vids with these guys
You live by them?
Deep Purple=AWESOME COLORS=AWESOME BAND= Deep Purple
Let's see him do that with his left hand 😏😎
@@Pvt._Liquor that's the goal my brain is left handed so we help each other its like learning all over again lol keeps you humble God bless
Nice job abe! Dude that Everlast looks like they've updated it a little, front interface has changed...looks better!
It's been redisined inside and outside
@@goldeneagle_wld245 it's due time they did, the old model was like 10 years old
Awesome video Abraham! Just keep an eye out for that "undercust" keep up the great work guys! :)
Noted on the undercust😂😂
Good info, thanks for sharing. 👍👍👏🏻👏🏻👏🏻👏🏻
excellent technique
congratulations my friend!
if you use a tig torch with no tungsten you can get gold like nuggets on your plate but it will break the cup most likely
Very great job
Great video but the fact that your on XS pipe and larger bore helps tremendously with color… we need one of how to maintain proper color on 2 ,3,4 inch school 10 stainless lol that’s where the lord’s work is done… 🙏
Great work, I appreciate 🌷🌹💐
I’ve actually been having problems welding lately. On my most recent job I’ve been doing mostly stainless, schedule 10, and a lot of small diameter. I suppose it’s important that I mention I am still fairly new in the field. I tend to get deep reds in my welds which tells me I’m very near burning the stainless up. The problem is, sometimes I get it even when I strike up on a cold pipe. My coworkers say it’s because my tungsten isn’t out far enough and I’m moving too slow. Do you have any thoughts or anything to add to the reasons I’m getting these colors?
how did u fix the issu?
Great content. I'd like to see more videos, like stainless stick welding or more fab vids.
Good cup
I recently work with stainless stell pipe, mostly thin pipe like sch 20 to sch 40, when doing welding on flange the color is show up but when welding on the pipe joint there is no color, jist dark grey, still figured it out why
Like the dewar flask.
Thats clean
Nice final
Believe it or not I worked for ETS in a fab shop all stainless and exotic metals, never touched a tig rig, I was a helper then slowly learned how to tack, then I was a tacker then learned how to throw a root in stainless and kept moving forward and now I struggle to learn stick, I can throw a root w 6010 but it ain’t all that slick, detailed tutorial? Root-Cap 6010/7018 ?
They got an older video about that
The way you angle you’re rod , whipping pattern being consistent and amps when I was in high school my teacher told me to whip it and hold In the puddle for one second then go out , keep you’re eyes at the weld I had the bad habit of watching the rod leave then would loose my straight line
Nice consistency man you got that golden arm! I'm practicing on plate right now, in that frustrating learning phase, many many hours to go. Eventually it'll click hopefully! Your guys tips have been very helpful
How is it now?
@@mrillis9259 It's like riding a bicycle, when you get that motion down it's all muscle memory. Unfortunately I went Aerospace and there is no walking the cup due to the scratching of base material.
Best Job Bro)
Awesome 👍
I would just use a 12 cup to get better gas coverage
Do you have a social?
New vid let’s goooo🔥
Thanks for sharing bro!
Purple is to hot… the puddle made contact with the atmosphere before it had the chance to completely solidify
how is it you are getting less and less heat affected welds when welding over the same hot area? i wish someone could teach me how to walk the dog to get these welds, i have a test for 3" nom 304 pipe with a 1/16 gap but my weld was greyish and not good , idk if it was the metal or im just not good standing and trying to weld this out of position as i said perhaps if i knew the dog trick it would be a better weld
Important info to understand what your metal is doing as the heat goes up. Great video and beautiful consistent welds. Are the colour changes evident in all metals when welding or only on stainless steel?
What's your gas flow cfh?
Looks awesome man
Them HH boots looking slick
Everlast 250 EX HF IGVT I got it have it for Christmas love it 😍
Nice work 👏🏿👏🏿👏🏿
Travel speed is the key!
Where can I buy me a cool looking welding cap like the one you have , Abraham ?
Bought mine from a woman who makes them on etsy
Awesome video thanks 🔥 just like warm apple pie 🥧 🤣
What do you use to video while you weld? Do you put a weld lens in front of the camera?
so why dont you show how you can make the gold color right off the bat from the first weld?
Beautiful welds
Thank you bro usfull video
Weer can I get safety boots like those?
Кроме этих движений других не существует. Плагиат. Нет ничего нового под солнцем. Кто следующий?
Hello. My name is Sasha. I'm from London. I like your approach to teaching. But you always miss the point. And the main thing is when you need to show the wire feed manually. How to hold the wire in your hands. Position of legs and body. And the most important thing is the manipulation of the hand. And it would be nice to show it all in one video and close-up. I hope that many beginner welders will be grateful to you. Thank you for understanding.
Love this. I can never get that pattern. I'm a student and haven't figured it out yet. Any tips
Practice make the Master
@@goldeneagle_wld245 your right I do any chance i get. I'm not sure the motion to get that pattern. Any tips
@@aprillawless4746 imagine walking a barrel down the street. Now do that with a tig cup.
@@xXxAtkinsxXx ya for some reason I couldn't get it to walk always wanted to hang up and not move. Now I'm out 2 months with elbow and hand surgery.
What if it comes out black?
Máximo respeito top top good
Great video Abraham 🤘🔥
What weld lens are you filming through?
Nice nice
Where do you guys get those welding caps
Why 176?
Turn the gas up for a gold color.
Hey man, how do I get gold on something 3mm thick 😅
Great video but how do you do this on sch 10? 😬 Serious question. Thanks.
👍👍👍👍👍👍
MANTAP JIWA👍
I weld on 300 amps at work
*You can’t weld*
Can you do more stick welding videos??!plz
If I'm a welder. Do I have to start talking like I'm in Hip Hop video?
Jo jo whats up man 😂😂😂
It's not funny to mock people. These teachers are professional in their work and in educating.
😍😍😍👍👍👍
I love my 250EX have paid for itself thrice over
Can you monitor color change through the lens or do you have to stop to observe it?
Use a gold lense and you can see the width of the HAZ either side of the cap, yes. Cant see it so well with a green glass filter lense
@@kf8575 Thank you; I can see it now. I didn't know about the gold lens. Now that I have tried it, I can also see the colors of the HAZ through my auto lens, although that requires a fine adjustment of shade level, which is hard to guess without testing.
Awesome! What size filler rod?
1/8"
well lets do it on a 1 inch sch 40 stailess steel pipe ,, from 6 o clock to 12 o clock with a regular machine just dc machine out on the field lets go lets say a clasic 300 lincols diesel ????
Blue is actually alot hotter than the wheat gold color not the other way around.
That was a BUUUUUURRRRRRNNN
Thats a sus lookin apple pie
So grey and purple and blue , are not a favorite color , but do they pass the X-ray
Or grey a sign of poor welding besides a ugly non favorite color for a cap ??
It will pass xray, but if it’s burnt to much you will lose nickel content which is what aids in the corrosion resistance of stainless. Which basically defeats the purpose of using stainless to begin with.
Brother, i cant get that movement in butt joint, can u plz give any advice for me
Pls do 3f im 13 and need help with it
Ex gfs really don’t know how to communicate🤣🤣
Скользит керамика по трубе, почему?
Как вариант - от перегрева шва может скользить. А так - есть способ - на лепестковом круге на болгарке поточи немного торец сопла, только на небольшой скорости, скользить перестанет
@@mddenis1 спасибо тебе, буду пробовать
Hey weldtube, i could make russian subs/translations of your content for you, are you interested? I'm a pro welder, so I know the subject well
Yeah man, we would definitely be interested. Send us an email to info@weldlife.com Thanks!
First
I think its pumpkin.
How come every guy in this shop acts like a thug gangster. Just show us how to weld. Be normal.
Its H town.a lot of people are like that.
There is no such thing as getting gold. You're only getting a gold color. It's not real gold.
I'd like to see how much penetration that weld has .....it sure looks pretty....🤔