Lots of comment here about whether this method provides sufficient penetration and strength, and how welds must always be continuous. Wrong. In fact the widely practiced, and accepted, method of joining thin sheet metal for auto body repair is a serious of MIG tack welds. I would welcome a test-to-failure demonstration of the strength of the welds shown here compared to the superior methods claimed in the comments. No doubt a precision TIG weld would win, but I suspect that a lot of us have made continuous welds that we think are hugely stronger, but aren’t. The other issue is product application. We make decisions every day as to the appropriate strength of joined materials. That slender piece of wood trim is attached with a tiny, slender nail that is “weak” but provides the necessary strength and appearance; that wall is framed with 16-penny nails fired by a big nailer. No, I sure as hell wouldn’t use the welding method here for an aircraft engine mount, but for a table stand with welds ground smooth for appearance the rod arc welding shown here would be indestructible. Anyone who welds should know the principles of heat, speed, penetration and strength, especially for crucial applications. But to immediately dismiss what is shown here based on theory without empirical proof is bad science.
Those "test-to-failure demonstrations" are done all the time in welding schools, and I'm sure there are plenty on CZcams. They show conclusively that these welds are weaker. What he does here is fine for something that doesn't bear a load. He's contaminating the puddle with flux again and again. He's heating, cooling, heating, cooling...again and again. You can not get away from physics--the weld will be more brittle than a continuous bead, even if he were to magically get the same penetration. MIG doesn't use flux and thin auto body sheet metal is welded for appearance, not strength. I don't think the MIG comparison works. I admit that I am a terrible welder, so take my comments with a grain of salt.
@@darinclay6838 Those are good points, and it sounds like our welding skills are similar. Every time I make a weld that might actually hold two pieces of steel together for a few hours I stare at it in amazement. I have seen those weld test vids but not one that looks at this oddball method specifically.
Не хватает 4-й скорости для просмотра такого пустого контента.Надо же,растянуть минутный видос на 5.44 мин.Респект,и ещё полляма просмотров набрал!Просто Спилберг!!
@@user-jp1jq1pc4z Прихватываешь посильнее фиксирующий кусок трубы, чтобы не развалилась вся конструкция и крути вокруг своей оси. Или обходи и подлезай со всех сторон. В чём проблема?
This seems to run a bit contrary to things I was shown when I worked with experienced engineers in a workshop - Use magnet then g clamps or f clamps to hold in place - tack the 2 outside corners then the 2 inside corners and then weld the outside line first then the 2 outside to inside lines then the inside line last
@mckyvr The way you say it is what I was taught long ago--the metal is less likely to warp. I'm not a good welder, but I remember the lesson well, "An ugly, strong weld is way better than a pretty, weak weld, but if you practice, you don't have to choose." This method of doing lots of little tack welds is catching on because the welds look nice, but if you're doing anything that requires strength, you'll be disappointed with the results. The guy making the vid has other work where he does structural welds and does them right, but if you are just doing some ornamental work, then this is fine.
Continuous weld, turn the amps down or speed up or both. Don't weld like this latest internet trend, you will not get any penetration. Welds like that on something structural could kill someone. Learn to weld properly.
I think this kind of welding is fine for something decorative- I would use wire if rods kept burning through. I have trouble getting rods started at lower amperage settings.
@@dudeb5610 There are hundreds of videos on CZcams on how to weld properly far better than me, but if you want me to show you hop on a bus, I am a coded welder . My point is don't show people how to do something unless you are qualified to do so. Monkey see's, monkey does. If someone copies that style to weld a car for eg that weld will fail and they could kill themselves or someone else. How would you feel if members of your family died because some Burk with a welder bodged his suspension up and crashed into another car on the first bend in the road he came across due to weld failure . You've only got to read all the comments on here. " Thanks excellent job"
Lo "ideal" es que el tamaño del electrodo sea igual o menor que el espesor de la chapa a soldar. Por lo tanto deberías usar electrodo de 2mm. Se puede soldar tranquilamente con uno de 2.5mm, pero requiere de mas experiencia porque necesita mas amperaje y por lo tanto desarrolla mas temperatura pudiendo hacerse "huecos" que luego hay que rellenar.
I would tack the corners, then weld the outside corner ( the least pull), then the sides starting in to out and finally the inside corner ( this has the most pull).
Вообще-то если так разбираться то так варить нельзя. Так варят. Но деформация метала будет, поэтому швы делают с разных сторон и желательно не полный для снятия напряжения в метеле.
Ещё большой угол наклона электрода,поэтому на концах были поры.В верхнем остром конце лучше сделать пропил диском двоечкой и варить горизонтом,а не вертикалом.
Неплохо для начала. Все начали правильно, поставили мост . Варить надо углом назад тогда будет обратный валик , да и попробуйте основными , от рутиловых шлака много .
По моему даже начинающий сварщик знает, что варить можно: 1 - без поперечной трубы, достаточно иметь магнит и ровную поверхность; 2 - противоположные швы накладываются в противоположном направлении; 3 - перед наложением шва смежного с предыдущим (швы смыкаются концами) нужно отбивать шлак с уже наложенного; 4 - перед наложением швов прихватки делаются сразу со всех сторон
А то, что при сварке применяются краги, а не вязаные перчатки сварщик знает? И почему? А еще, если уж приспичило закреплять помимо магнита и прихваток, есть какой-то инструмент, название начинается на "струб" и заканчивается на "цины", говорят, он доступен не только опытным сварщикам. А еще непонятно, зачем магнит вообще, если соединять допустимо с точностью до 90 градусов? Да я с помощью простого угольника точность в 10 градусов обеспечу на глаз!
когда искал инфу каким электродом варить , попадалось что до 3 мм метал варится электродом 2-2.5 , а у вас 3 мм , так каким все таки электродом луче и проще варить метал 2.5 мм ? сколько ампер и где + сидит ? можете сказать ?
are you his colleague, friend or maybe partner?? do you really like what he did?? seriously this is a beautiful job for you?? either you're in love with him or you're blind, and you're definitely ignorant because you can't see the complete fucked up work done by an ignorant with a big ego everyone I know after seeing a fragment of this film asked what kind of child did it, because a grown man was ashamed to show it complete shame and you still say great job... did he give you a blowjob??
@@tjguzik I tried to do what he did in the video but couldnt. His way looks ok for what I want even if is not up to your pedantic standards. Now, go make your bed and stop being stupid to people.
doing one bead causes metal to get hotter which will result in burn through. Spot/tack welding allows a thick bead as long as you do it while the bead is still hot.
Das Problem an der Sache ist, dass man von innen nach außen Schweißt, dass die Wärme nach außen geleitet wird. Hier falsch gezeigt. Zum anderen die Kehlnaht welche für den Verzug verantwortlich ist, da hier das meiste Material vorliegt und viel Wärme speichert. Ich habe Winkel auf dem Schweißtisch gefertigt die festgespannt waren. Auch hier gibt es trotzdem leichten Verzug. Es kommt immer auf das Material an, was man schweißt. Schweißen und komplettabkühlen lassen kann auch zu Verzug führen trotz verspannen. Besser geht das als Viereck aber auch dort kann je nach Größe Verzug auftreten je länger die Seiten werden. Das sieht man ab einer bestimmten Länge wo sich das Material leicht nach innen durchbiegt. Hier hätte er am Ende kontrollieren sollen statt Daumen hoch....ich hätte Wetten können...
Cheers. I agree but it n site we all know everyone is in a hurry and for that weld to do it nicely like this isn’t always possible. Has anyone else ever worked as a welder for a company and your supervisor doesn’t know anything about metal and where you should weld and where a weld would actually weaken the structure not add to its strength. Or they want you welding over paint and grease and shit. I put up with it for a year then my pride returned and I went to a proper shop again. Lol. Maintenance welding for a Ready Mix Plant is pure hell.
Tengo esta escuadra magnética, la mas grande. Y el problema que tengo es que tiene tanta fuerza el imán que no queda la soldadura, tengo que hacer 2 o 3 puntos y después sacarla porque es como que el caño rechaza el material de aporte por el imán.
depende mucho del peso del material, si es para union de tubos delgados y poco pesados es mejor usar los imanes mas pequeños, Otro punto, es que el iman jala la soldadura, Pero si tienes buena calidad electrica, es mas sencillo de controlar ese incoveniente, saludos.
si no sabes molar como vas a saber soldar no debes clavar la mola al perfil porque cuando lo pintas se ve todas las marcas de la mola llevo 44 años soldando y creo que te falta experiencia
This video is not to teach or patronize but just to share experiences. hopefully useful and hopefully healthy friends 🙏
No kidding you don’t know the difference between tube steel and pipe.
Na koliko ampera se postavlja aparat za ovakve cevi?
Ещё большой угол наклона электрода,поэтому на концах были поры.В верхнем остром конце лучше сделать пропил диском двоечкой и варить горизонтом,а не вертикалом.
@@genagoga6185а что от того что если будут поры или нет, качество сварки изменится или это повличет на что то 😂. Вода потечёт..
@@mio-gh1wkтак можно и "винограда "насрать,то же держать будет.
Lots of comment here about whether this method provides sufficient penetration and strength, and how welds must always be continuous. Wrong. In fact the widely practiced, and accepted, method of joining thin sheet metal for auto body repair is a serious of MIG tack welds. I would welcome a test-to-failure demonstration of the strength of the welds shown here compared to the superior methods claimed in the comments. No doubt a precision TIG weld would win, but I suspect that a lot of us have made continuous welds that we think are hugely stronger, but aren’t.
The other issue is product application. We make decisions every day as to the appropriate strength of joined materials. That slender piece of wood trim is attached with a tiny, slender nail that is “weak” but provides the necessary strength and appearance; that wall is framed with 16-penny nails fired by a big nailer. No, I sure as hell wouldn’t use the welding method here for an aircraft engine mount, but for a table stand with welds ground smooth for appearance the rod arc welding shown here would be indestructible.
Anyone who welds should know the principles of heat, speed, penetration and strength, especially for crucial applications. But to immediately dismiss what is shown here based on theory without empirical proof is bad science.
Agreed. Many people on here don't know what theyre talking about.
MIG tacking, not stick tacking. Big difference
Those "test-to-failure demonstrations" are done all the time in welding schools, and I'm sure there are plenty on CZcams. They show conclusively that these welds are weaker. What he does here is fine for something that doesn't bear a load. He's contaminating the puddle with flux again and again. He's heating, cooling, heating, cooling...again and again. You can not get away from physics--the weld will be more brittle than a continuous bead, even if he were to magically get the same penetration. MIG doesn't use flux and thin auto body sheet metal is welded for appearance, not strength. I don't think the MIG comparison works. I admit that I am a terrible welder, so take my comments with a grain of salt.
@@darinclay6838 Those are good points, and it sounds like our welding skills are similar. Every time I make a weld that might actually hold two pieces of steel together for a few hours I stare at it in amazement. I have seen those weld test vids but not one that looks at this oddball method specifically.
Obrigado pela dica. Na próxima, mostre a amperagem da máquina.😉
Muy buen detalle de como soldar una unión con caños finos a 90°. EXCELENTE !!!! Gracias !
Fiou top top... qual a AMPERAGEM que vc usou para fazer essa solda parceiro?
Y que electrodo uso
Не хватает 4-й скорости для просмотра такого пустого контента.Надо же,растянуть минутный видос на 5.44 мин.Респект,и ещё полляма просмотров набрал!Просто Спилберг!!
Ещё и с двумя огрызками труб, показал бы с большой конструкцией как её крутить вокруг своей оси !!!
@@user-jp1jq1pc4z Прихватываешь посильнее фиксирующий кусок трубы, чтобы не развалилась вся конструкция и крути вокруг своей оси. Или обходи и подлезай со всех сторон. В чём проблема?
Уже лям просмотров с хвостиком! Спилберг просто отдыхает!🤣🤣🤣
@@remont_kvartir_v_samare УЖЕ 1,5 ЛЯМА)))
@@user-jp1jq1pc4z да оленевод он, а не сварщик, (учитель блин..)
Good vídeo, inverter machine? How do you calc amperes? Electrode type?
This seems to run a bit contrary to things I was shown when I worked with experienced engineers in a workshop
- Use magnet then g clamps or f clamps to hold in place
- tack the 2 outside corners then the 2 inside corners and then weld the outside line first then the 2 outside to inside lines then the inside line last
There’s a hundred ways to do it
@mckyvr The way you say it is what I was taught long ago--the metal is less likely to warp. I'm not a good welder, but I remember the lesson well, "An ugly, strong weld is way better than a pretty, weak weld, but if you practice, you don't have to choose." This method of doing lots of little tack welds is catching on because the welds look nice, but if you're doing anything that requires strength, you'll be disappointed with the results. The guy making the vid has other work where he does structural welds and does them right, but if you are just doing some ornamental work, then this is fine.
Disculpe que electrodo usa?
Grscias ,,gracias ,gracias por enseñarnos ,,,Diós te cuide y proteja siempre
Que dimensiones tiene ese estructural cuadrado?
Qual a amperagem?
Continuous weld, turn the amps down or speed up or both. Don't weld like this latest internet trend, you will not get any penetration. Welds like that on something structural could kill someone. Learn to weld properly.
show us then on how to weld properly
I think this kind of welding is fine for something decorative- I would use wire if rods kept burning through. I have trouble getting rods started at lower amperage settings.
@@TheMarpalm With wire I'm having no trouble doing a continuous weld on pipe like this (I'm a self taught crappy welder).
@@dudeb5610 There are hundreds of videos on CZcams on how to weld properly far better than me, but if you want me to show you hop on a bus, I am a coded welder . My point is don't show people how to do something unless you are qualified to do so. Monkey see's, monkey does. If someone copies that style to weld a car for eg that weld will fail and they could kill themselves or someone else. How would you feel if members of your family died because some Burk with a welder bodged his suspension up and crashed into another car on the first bend in the road he came across due to weld failure . You've only got to read all the comments on here. " Thanks excellent job"
@@kaasmeester5903 I am the same. Wire seems to be the way to go on thinner stuff like this.
Qual tipo de amperagem ta usando nesse tipo de metalom ,so por curiosidade. Mas ficou muito .
60 amp
Qual amperqgem usa? E qual eletroudo?
Hola felicidades por el video, tengo una duda es recomendable soldar con varilla gruesa o delgada tubo perfil de 2 milímetros
Lo "ideal" es que el tamaño del electrodo sea igual o menor que el espesor de la chapa a soldar. Por lo tanto deberías usar electrodo de 2mm. Se puede soldar tranquilamente con uno de 2.5mm, pero requiere de mas experiencia porque necesita mas amperaje y por lo tanto desarrolla mas temperatura pudiendo hacerse "huecos" que luego hay que rellenar.
@@MartinLopez-nt9kcexactamento
как всегда в комментах больше и полезней информация !)))
Esas escuadras magnéticas son una belleza
Question, What was your welder settings on for this weld?
Where it makes sparks.😄
I would tack the corners, then weld the outside corner ( the least pull), then the sides starting in to out and finally the inside corner ( this has the most pull).
Cómo se llama esa pieza Para cuadrar
@@fredymoralesfigueroa3284escuadra
Thanks for sharing. I believe that is 16g steel, what electrode are you using here?
Thanks
Вообще-то если так разбираться то так варить нельзя. Так варят. Но деформация метала будет, поэтому швы делают с разных сторон и желательно не полный для снятия напряжения в метеле.
Ещё большой угол наклона электрода,поэтому на концах были поры.В верхнем остром конце лучше сделать пропил диском двоечкой и варить горизонтом,а не вертикалом.
Интересно получается, что значит угол проварить не полностью? И отопление так варить будешь?))) Автор всё сделал для того, что бы удержать угол.
C'est trop beau la soudure quand c'est bien foutu 👍😁
If it is stainless material ?
Very satisfing to watch,, I use this technique with our MIG welder
Thanks brother
Bnyak cara..tapi sama tujuannya ya bang. Terima ksi bnyak. Sudah ksi pembedaan dari yng lain 👍🤝
Good work 👍👍
Неплохо для начала. Все начали правильно, поставили мост . Варить надо углом назад тогда будет обратный валик , да и попробуйте основными , от рутиловых шлака много .
Y porque cuando soldo en angulo de90 al terminar se tuerse se descuadra o se enchueca
Всеравно потянуло метал Потомучто в конце ролика не показал как проверил угол.Метал такая вещь нету Трех точек опоры значить ДЕФОРМИРУЕТ
Конечно, уголком зря не проверил итог, да. Но потянуть не должно было за счёт прихваченной диагонали.
какие электроды использовал ?....и какой ток сварки ?..
яким фільтром для камери ви користуєтесь?
Protección?
По моему даже начинающий сварщик знает, что варить можно: 1 - без поперечной трубы, достаточно иметь магнит и ровную поверхность; 2 - противоположные швы накладываются в противоположном направлении; 3 - перед наложением шва смежного с предыдущим (швы смыкаются концами) нужно отбивать шлак с уже наложенного; 4 - перед наложением швов прихватки делаются сразу со всех сторон
Что такое "призывники"? Я не сварщик, но интересно.
@@UlexPapov это опечатка, уже исправлено
@@St.Eg. Спасибо. Теперь понятно. А то я думал, что это что-то мне незнакомое из терминологии сварщиков :)
@@UlexPapov 😁
А то, что при сварке применяются краги, а не вязаные перчатки сварщик знает? И почему?
А еще, если уж приспичило закреплять помимо магнита и прихваток, есть какой-то инструмент, название начинается на "струб" и заканчивается на "цины", говорят, он доступен не только опытным сварщикам.
А еще непонятно, зачем магнит вообще, если соединять допустимо с точностью до 90 градусов? Да я с помощью простого угольника точность в 10 градусов обеспечу на глаз!
Hola, ¿puedes darme las dimensiones para hacer un ángulo recto redondeado por favor, gracias?
когда искал инфу каким электродом варить , попадалось что до 3 мм метал варится электродом 2-2.5 , а у вас 3 мм , так каким все таки электродом луче и проще варить метал 2.5 мм ? сколько ампер и где + сидит ? можете сказать ?
Лучше и проще будет полуавтоматом и проволкой 0,8 мм.
wow. beautiful work. Thank you for sharing your skills.
are you his colleague, friend or maybe partner??
do you really like what he did??
seriously this is a beautiful job for you??
either you're in love with him or you're blind, and you're definitely ignorant because you can't see the complete fucked up work done by an ignorant with a big ego
everyone I know after seeing a fragment of this film asked what kind of child did it, because a grown man was ashamed to show it
complete shame
and you still say great job...
did he give you a blowjob??
@@tjguzik I tried to do what he did in the video but couldnt. His way looks ok for what I want even if is not up to your pedantic standards. Now, go make your bed and stop being stupid to people.
Excelente demostración
Gracias por la enseñanza
That was awesome!
Cuanto de amperaje sueldas, soldé con 40 y hice hueco :(
good smooth job
No es mejor hacer costura que puntadas?
Hi if we want Make Square we have to weld Four sides???
Uh…….huh?????
You have to make it square when you tack it. Before the welding. That’s why he put the brace there to keep it from distorting/warping
I'm still learning but continuous weld on thin metal? penetration? Burning a hole is what you'd like to prevent ain't it?
Try to pulseweld if your weldingmachine is able to do, this is also possible with stick welding ( if you have the equipment )
Yes, this technique he is using is to prevent burn through which will happen if trying to do a continuous bead on thin wall.
Спасибо тебе молодец
love this guy pls upload more and continue to share thanks
You're welcome
Muchas gracias por su enseñanza
What is the angle length.??
Friend How Many AMPS Do You Have It ???
Amén.
I did not know that charles chaplin in his time had published videos of his secret passion for welding :)
Why do you make single spots instead of one bead?
doing one bead causes metal to get hotter which will result in burn through. Spot/tack welding allows a thick bead as long as you do it while the bead is still hot.
Because this is thin wall steel, it WILL burn through regardless of which amps you are using.
Confident welder
This is a joke right? 🤣 this man Cant weld this is a shitty weld you need to weld in 1 pass not like a Bird that shits and shits
Диаметр электрода 2, какая фирма сварки?
A pesar de que no eres soldador profesional te quedó bueno.
I always imagined I should do it this way😎.
Thanks brother 🙏
Ampere??? And 6013 2.5m ??
Winkelüberprüfung????
Ich garantiere, dass der sich verzogen hat!
Trotz der angeschweißten Diagonale?
Das Problem an der Sache ist, dass man von innen nach außen Schweißt, dass die Wärme nach außen geleitet wird. Hier falsch gezeigt. Zum anderen die Kehlnaht welche für den Verzug verantwortlich ist, da hier das meiste Material vorliegt und viel Wärme speichert. Ich habe Winkel auf dem Schweißtisch gefertigt die festgespannt waren. Auch hier gibt es trotzdem leichten Verzug. Es kommt immer auf das Material an, was man schweißt. Schweißen und komplettabkühlen lassen kann auch zu Verzug führen trotz verspannen. Besser geht das als Viereck aber auch dort kann je nach Größe Verzug auftreten je länger die Seiten werden. Das sieht man ab einer bestimmten Länge wo sich das Material leicht nach innen durchbiegt.
Hier hätte er am Ende kontrollieren sollen statt Daumen hoch....ich hätte Wetten können...
Как вариант.
Но если хотите чем то поделиться, поясните толщину стали, силу тока, марку электрода.
Толщина 1.5-2мм, 80-100 ампер
Специалисты, это хорошая техника сварки?
Excellent job.
I think the title should be: how to weld to look like a beginner.
Or how about. How not to weld for beginners. No matter how thin the steel is.
A ver si entendí. Osea que aconsejas soldar un PTR cal 14 punto tras punto? En el cal 14 me los aviento corridos los cordones🙄
Carnal, el PTR es Perfil Tubular Redondo, y en el video creo no es redondo 😅
@@brianpatino4123 pensé q era perfil tubo rectangular
Grind adjoining edges to give the weld more surface to burn to!
Thanks
Wszystko bardzo dobrze. Lecz przy szlifowaniu musi być osłona na szlifierce👍
una observacion, no hay que soldar con guantes de algodon es peligroso mejor usar los adecuados.
Nice tutor...🙂👍👍
Thanks brother 🙏
Ты так год варить будешь, а зажимы в твоей стране не продают?🤗😆
Itu pake api berapa kalo boleh tau?
Очень крассива и качественно 👍👍👍👆Браво!!!
Joss 🙏🙏
Salam sehat dan sukses selalu ya bos 🙏🙏🙏salam pemula ilmu bermanfaat bos 🙏🙏
Excelente queda reforzado
Thanks brother 🙏
Cheers. I agree but it n site we all know everyone is in a hurry and for that weld to do it nicely like this isn’t always possible. Has anyone else ever worked as a welder for a company and your supervisor doesn’t know anything about metal and where you should weld and where a weld would actually weaken the structure not add to its strength. Or they want you welding over paint and grease and shit. I put up with it for a year then my pride returned and I went to a proper shop again. Lol. Maintenance welding for a Ready Mix Plant is pure hell.
В смысле как? Берешь полуавтомат и варишь с прихватками. Делов на 2 минуты. А эта парнуха с не проваром, это только для вида.
Cómo se llama el electrodo para soldar perfiles delgados?
Puedes usar 3/32 en 6013
Такое ощущение, что ты недавно варить начал. Много ошибок, и именно ошибки новичка. Видно сразу.
MUY HECHO EL TRABAJO SOLO FALTA ALGO MUY IMPORTANTE... EL EQUIPO DE SEGURIDAD PERSONAL EN EL EQUIPO Y GUATES DE TRABAJO
Cierto, la guarda del esmeril es importante
i spot like this.i dont do full weld cause the wire of my holder will get hot easily
Я все полуавтоматом варю, вообще уже давно электроды в руки не брал.
Rod किती mm चा आहे?
2,6 mm brother
Tengo esta escuadra magnética, la mas grande. Y el problema que tengo es que tiene tanta fuerza el imán que no queda la soldadura, tengo que hacer 2 o 3 puntos y después sacarla porque es como que el caño rechaza el material de aporte por el imán.
claro porque son solo para hacer puntos sino te desvía el arco
@@unomismo4510 Wow! cosas que ni se imagina uno, pero tienen sentido! 🤔
depende mucho del peso del material, si es para union de tubos delgados y poco pesados es mejor usar los imanes mas pequeños, Otro punto, es que el iman jala la soldadura, Pero si tienes buena calidad electrica, es mas sencillo de controlar ese incoveniente, saludos.
Tengo el mismo problema.!!!😁
Без фаски, да еще после зачистки сварочный шов в фольгу преврвщается...
EXELENTE PARABENS
Thanks brother 🙏💖
What Amper user, please?
80amper brother, e6013 2,6mm
Muchas gracias por el video… 🎉
Обычно я так и варю, только я не сварщик.
Nice Work.
Thanks brother
si no sabes molar como vas a saber soldar no debes clavar la mola al perfil porque cuando lo pintas se ve todas las marcas de la mola llevo 44 años soldando y creo que te falta experiencia
Отвратительное качество сварки, внешние углы запиливать нужно, шов в канавку должен укладываться, в место этого гигантский наплыв.
Отличный метод.
А в чем состоит метод-то?
ставлю два «лайка» еще и за то, что в ролике не звучит какая нибудь дурноватая музыка
Kawatnya pake merk apa om
Merek nk bang
А где советы по электродам?? И силе тока??
Que número de electrodo es ese
2013
Esta muy fuerte esa eléctrica
Muito bom
А ещё лучше, сжать угловой струбциной.
Ótimo
А разве фаску перед сваркой не надо делать?