How to Nickel Electroplate at Home | bit-tech Modding

Sdílet
Vložit
  • čas přidán 16. 07. 2020
  • Want to spruce up some copper or brass components? Or perhaps you want to re-finish a worn out block? This is the tutorial for you.
    For quick reference:
    To make the electrolyte - I used 32V at 3A, will work at lower but will take longer
    For acid pickle - I used 5mol HCl which I diluted to roughly 0.2-0.5mol with water for 5 minutes
    For Plating - I used 4.5V for this part with a distance between it and the anode of about 10cm
    For Plating - Connect POSITIVE to ANODE and connect NEGATIVE/GROUND to PART
    Timestamps:
    00:33 - Intro
    02:30 - Materials
    06:30 - Making the Electrolyte
    12:50 - Cleaning
    14:56 - Acid Pickle
    16:54 - Plating Intro
    18:33 - Plating Method
    23:30 - Final Thoughts
    ____
    Materials used in this guide:
    Nickel Anodes (thin): amzn.to/2WuPzsx
    Glass Beakers: amzn.to/2CejAG9
    White Vinegar: amzn.to/2Wuhetv
    Power Supply: amzn.to/30s1it4
    Copper Wire: amzn.to/3jcVM5W
    Funnels: amzn.to/3h80VdI
    Filtre Paper: amzn.to/30pqHUd
    Ultrasonic Cleaner: amzn.to/3eBS0zp
    Cleaning Fluid: amzn.to/2Cm36vv
    Magnetic Stirer: amzn.to/3jhfSfe
    HCl Acid from: apcpure.com/
    Source locally and responsibly.
    ____
    Link to our webshop:
    store.bit-tech.net/
    ____
    Don't forget to follow us over at:
    Website - www.bit-tech.net/
    Instagram - / bit_tech
    Discord - / discord
    Facebook - / bittech
    Twitter - / bittech
    Builds.gg - builds.gg/bittech
  • Hry

Komentáře • 377

  • @0815Skorpio
    @0815Skorpio Před 3 lety +49

    Pro Tipp: Constant Current works better then Constant Voltage and low Current takes longer, yes but it will be more even and precise. I do Nickelplating for a living. And no i can´t plate your parts because I am not allowed to take any random stuff, we dont do that. We plate grinding tools for CNC-Precisiongrinding. As pointed out in the Video for best Results Clean Parts are the most difficult part of the plating.

    • @bittech1
      @bittech1  Před 3 lety +5

      Martin Brieger That’s a handy point. I had hoped to do exactly that but it seems the unit I chose is voltage controlled rather than current :/

    • @JaenEngineering
      @JaenEngineering Před 3 lety +4

      @@bittech1 set the voltage higher and then set the current limit and the power supply will adjust the voltage down to whatever is necessary to maintain the current. If the voltage is limited and isn't high enough to push the set current, it'll just maintain the voltage at a lower current. It all comes down to the resistance of the electrodes/electrolyte. The higher the resistance, the more voltage you need for a particular current and vice versa

    • @0815Skorpio
      @0815Skorpio Před 3 lety +3

      @@bittech1 as @Jamie Foster pointed out, solution is crank the voltage up as high as possible and just set the current as high as you want.

    • @olivernavarro6237
      @olivernavarro6237 Před 3 lety

      Do you have a recommended device ?

    • @mahamedshata3031
      @mahamedshata3031 Před rokem

      I need some help I do that for living to iam Egyptian and I need help alot please

  • @scottdahlberg4890
    @scottdahlberg4890 Před 3 lety +6

    This is the best plating tutorial on the net.

  • @bittech1
    @bittech1  Před 3 lety +18

    Timestamps since this is a long boi:
    00:33 - Intro
    02:30 - Materials
    06:30 - Making the Electrolyte
    12:50 - Cleaning
    14:56 - Acid Pickle
    16:54 - Plating Intro
    18:33 - Plating Method
    23:30 - Final Thoughts

    • @janek-96
      @janek-96 Před 3 lety +2

      If you put them in the description youtube will automatically display them in the "progressbar"

    • @Anaerin
      @Anaerin Před 3 lety +2

      @@janek-96 Yes, IF the timestamps start at 00:00.

    • @IIGrayfoxII
      @IIGrayfoxII Před 3 lety

      Add these time stamps into the description a long wit 0:00 and take advantage of the time line chapter functionality youtube has

    • @sonoflysystrata2
      @sonoflysystrata2 Před 3 lety

      Ami not right in thinking there are extreme dangers if someone tries stainless steel? If the electrodes go around the wrong way do you not get toxic gasses? Might need a warning about that.

    • @sreekumarUSA
      @sreekumarUSA Před 2 lety

      @@sonoflysystrata2 Alex, the presenter, had warned about the matter; at the introduction about performing the experiment at a highly ventilated area. Common sense depicts the fact.

  • @AFvet1964
    @AFvet1964 Před 2 lety

    Definitely the best CZcams video on this subject that I've seen...and I've seen a lot of them!

  • @eighthof8
    @eighthof8 Před 2 lety

    The best plating instructional vid on youtube. Thank you for all the great detail!!

  • @networkingdude
    @networkingdude Před 3 lety +37

    Was staring and the bit-tech logo when I realize the 0's and 1's in the logo are 16 binary bits that gives you a HEX code of 554B which in turn converted to ASCII characters "UK"

    • @sreekumarUSA
      @sreekumarUSA Před 2 lety

      Bravo.

    • @reubenjustice9657
      @reubenjustice9657 Před 2 lety

      sorry to be so off topic but does any of you know of a trick to log back into an Instagram account?
      I somehow forgot the login password. I love any tips you can give me

    • @raylancamden6858
      @raylancamden6858 Před 2 lety

      @Reuben Justice Instablaster :)

    • @reubenjustice9657
      @reubenjustice9657 Před 2 lety

      @Raylan Camden i really appreciate your reply. I got to the site thru google and im in the hacking process now.
      I see it takes quite some time so I will get back to you later when my account password hopefully is recovered.

    • @reubenjustice9657
      @reubenjustice9657 Před 2 lety

      @Raylan Camden It worked and I now got access to my account again. I am so happy:D
      Thanks so much, you really help me out :D

  • @anthonypla7134
    @anthonypla7134 Před 3 lety

    Instant subcription. You made the process clear as mud for a beginner like me. Can't wait to have more time to check out your other videos.

  • @ezequieladrianminniti6252
    @ezequieladrianminniti6252 Před 10 měsíci +14

    Two suggestions: 1) Plating isn't about voltage, it's about current. 2) Always use magnetic stirring, or put multiple sacrificial electrodes at different locations, otherwise the plating WILL be uneven.

    • @janebickram4945
      @janebickram4945 Před 7 měsíci +1

      Reading your comment figured out you know aot about chrome plating, I want to chrome plate copper pipe about a Metre in length. How do I go about doing it

    • @redhed9776
      @redhed9776 Před 4 měsíci

      you actually dont need any current. Caswell has a new electroless way of plating. it works.

  • @klave8511
    @klave8511 Před 3 lety +4

    A lot of the talk about experimenting and “you might want to try” wouldn’t be necessary if you use current control of the plating. mA per square mm remains a constant if you want reproducible results with varying conductivity or concentration of solution. You power supply has that feature. This has been a very good introduction to plating, thanks.

  • @jdwilliams5244
    @jdwilliams5244 Před 2 lety +1

    Thanks for taking the time to explain how to plate.

  • @malcolmwatson6127
    @malcolmwatson6127 Před 2 lety

    Great video. Clear, thorough and well explained.

  • @sharkwithmanners1734
    @sharkwithmanners1734 Před 3 lety

    This video just gave me deja vu, I felt like I was back in 3rd year chemistry lol, love the content.

  • @ruftime
    @ruftime Před 2 lety +3

    Thank you!
    I recycle household plastic containers for plating/anodizing. Glass breaks too easily. Anything HDPE, which has the #2 recycling arrow. An under bed storage tub fits very large items😎

  • @The1PatSmith
    @The1PatSmith Před 3 lety +1

    Thank you, Alex, most interesting and informative. - Stay well.

  • @michaelrobinson9643
    @michaelrobinson9643 Před 3 lety

    More good fun for the diy inclined :). I'm envious of your workshop.

  • @justinwilliams4212
    @justinwilliams4212 Před měsícem

    by far the best video on the subject - thank you

  • @JonLloyd65
    @JonLloyd65 Před rokem

    This was just what I needed - thanks very much, very informative!

  • @johnnylightning5633
    @johnnylightning5633 Před měsícem

    I just found this. Yes old video but kudos, I love the attention to detail and I subscribed because of this vid.

  • @mandem9319
    @mandem9319 Před 3 lety

    Just in time for the weekend!
    Thanks for sharing all this information :-)

  • @exadorthecat3346
    @exadorthecat3346 Před 2 lety

    Best tutorial I've seen, thanks

  • @here-be-ember
    @here-be-ember Před 3 lety

    YESSSSS I saw the beaker in the last video and was waiting for this!

  • @korfenkeil
    @korfenkeil Před 3 lety +4

    For even better results you could try and find a big ring or even a hollow cylinder of nickel as the anode which could help with a more even finish and the shadows you mentioned

  • @respectanimals2
    @respectanimals2 Před 3 lety

    Excellent video , very thorough with all the information that I needed , 👍😎

  • @luissoto5942
    @luissoto5942 Před 2 lety +1

    Thanks for the time stamps

  • @Hongzbengkelspesialismatic

    Thank you for the knowledge that is shared and I hope you are always healthy and always successful

  • @guilhermecoelho5028
    @guilhermecoelho5028 Před 3 lety +10

    I just found out about your channel some days ago and man, you are so talented! I'm learning a lot and loving your explanations on basically everything you do. Probably won't ever do any of them because I lack the skills but you rock!

    • @user-is7es
      @user-is7es Před 4 měsíci

      Ah! A fellow American. We all lack skills. How do you build skills? 🤔
      You gotta start somewhere, don't you? Nobody ever started off as an expert in anything. Even this guy started off as a beginner at some point.

  • @frederickcooke8956
    @frederickcooke8956 Před 3 lety +5

    Very interesting and informative explanation of the process. Well done. Have you tried using citric acid for pickling? I use it for cleaning up small parts after silver soldering to remove residues. Any thoughts please?

  • @petewoodhead52
    @petewoodhead52 Před 2 lety +1

    Well done. Thanks for the learning!😃

  • @musicurio
    @musicurio Před 3 lety

    very interesting, and well presented and explained. Thanks!

  • @roybailey1134
    @roybailey1134 Před rokem

    Thank you for sharing your video , I really enjoyed it, I restore vintage carpenters plane's and vintage tools , so I wanted to try out some nickel plating, I will try it out a few times on less important things first just to get the hang of it, best wishes from a vintage Carpenter.

  • @4rs0nn
    @4rs0nn Před 3 lety +5

    Yaaas I can finally nickel electroplate at home! I’ve always wanted to do this.

    • @bittech1
      @bittech1  Před 3 lety +5

      You can also use this as a basis for brush plating btw, I didn't cover it in the vid for the sake of sanity though.

    • @endsemiscoming7204
      @endsemiscoming7204 Před 3 lety

      @@bittech1 Hey mate why didn't you made a GPU block though? I have been waiting for that kind of video forever 😆

  • @TurkeyJoe
    @TurkeyJoe Před 2 lety

    Great how-to, about to attempt my first plate on a watch case...

  • @AHollowVoiceSaysFool
    @AHollowVoiceSaysFool Před 3 lety +7

    Great video, very thorough instructions and good pacing. You may want to add that nickel compounds are carcinogenic so gloves might be good idea even before you get to the acid.

    • @eliwohl8734
      @eliwohl8734 Před rokem +1

      How about a mask for the vapors?

    • @FrippFrepp
      @FrippFrepp Před 8 měsíci +1

      @@eliwohl8734 Nickel is way too heavy and stable as an atom to leave in the form of vapours, the only vapour you are smelling is the acetic acid from the vinager

    • @1crazypj
      @1crazypj Před 2 měsíci

      It's also illegal pretty much everywhere to 'pour it down the drain' if you find you don't want to store solution as it's toxic waste.
      I've been told it's also pretty easy to find source of contamination back to exact house and courts like to 'set an example' so fines can be quite high..
      Where I used to live there was a Rexel plant about 4 miles away. I knew a plater there who said they would dump waste into river, pay fine and re-stock with fish every few years as it was still cheaper than paying for correct treatment and disposal.
      I'm guessing someone in local government found out or courts did some research as the fines got much much higher the 4th or 5th time they ended up in court (something like £2,000 initially to around £20,000 before plant closed down in 1990's)

  • @JH-sb1yd
    @JH-sb1yd Před rokem

    best video about plating thank you

  • @blackbear92201
    @blackbear92201 Před 2 lety

    Very helpful video. thanks for posting! :D

  • @guidoramacciotti3503
    @guidoramacciotti3503 Před 11 měsíci +2

    I really liked your video!! Im into restoring an old motorcycle and one thing i want to do is to nikel plate some of it's screws, so this comes really handy to see.
    Thanks!

    • @Sunrise.detailing
      @Sunrise.detailing Před 4 měsíci

      In planting process what kind of anode matarial use

    • @a-k-jun-1
      @a-k-jun-1 Před 3 měsíci

      In this situation nickel must be used. You must use the same material that the plating fluid is saturated with.

  • @Mr10usdad
    @Mr10usdad Před 2 lety

    Excellent video! Thank you!

  • @paulfitch9597
    @paulfitch9597 Před 2 lety +1

    Thank you sir. Video was fun.

  • @toptwitchclipz7928
    @toptwitchclipz7928 Před rokem

    i could not stop staring at this mans mustache, it is BEAUTIFUL.

  • @fthfdghfshfxdg4931
    @fthfdghfshfxdg4931 Před 3 lety +1

    I like that chill music

  • @RogerHyam
    @RogerHyam Před rokem

    Really great video. Thank you.

  • @munawargondal9318
    @munawargondal9318 Před rokem

    Rely ferfect and decent way to explane......

  • @jesurajv
    @jesurajv Před 3 lety +1

    Very informative and interesting. I am a hobbyist. I would greately appreciate if you could share how Nickel Foam coating can be done on steel plates? I guess the process would be more or less the same.

  • @timwarning9326
    @timwarning9326 Před 3 lety +1

    Awesome video Alex

  • @achannelhasnoname5182
    @achannelhasnoname5182 Před 3 lety +8

    Electroplating sure is easy, but getting an uniform surface finish can be pretty hard. I'm exited to see your results!

    • @SKMolloy69
      @SKMolloy69 Před 2 lety

      E5

    • @googlefirstnanegooglelastn1203
      @googlefirstnanegooglelastn1203 Před 2 lety +2

      I did high chrome plating for 10 years there is a lot of little tricks but there's not too much you can do to avoid thicker quantities of your plating materials towards the end or corners of the work you're trying plate covering the ends of material your trying to plate with aluminium or lead tape will bleed off excess copper nickel Chrome whatever the solution you're working with.

    • @bodeine454
      @bodeine454 Před 2 lety +2

      @@googlefirstnanegooglelastn1203 I'd like to have a visual of what you're talking about, using aluminum or lead tape, I don't quite understand how this would be done.

  • @antoniorodolpho6835
    @antoniorodolpho6835 Před 5 měsíci

    Congratulations very well done video!

  • @MechaNick03
    @MechaNick03 Před 4 měsíci

    You know this guy knows what he’s talking about with a moustache like that

  • @gargoyle7508
    @gargoyle7508 Před 2 lety

    "Whatever pH that is in there...."
    A true mastery of the GSE, this one.

  • @tartantam3405
    @tartantam3405 Před 2 lety

    Great video, thanks.

  • @kendavid4386
    @kendavid4386 Před 2 lety +1

    Very good video.

  • @saiko4477
    @saiko4477 Před 2 lety

    I testet it out and it worked great

  • @joe1569
    @joe1569 Před 2 lety +1

    Well done video

  • @dmprdctns
    @dmprdctns Před rokem

    Thanks... Very informative... Well done!
    Do you happen to know if steel can be plated onto steel?... Say, to fill in some pitting?
    Thanks again...

  • @paulmeynell8866
    @paulmeynell8866 Před rokem

    Excellent thank you really interesting

  • @deankay4434
    @deankay4434 Před rokem

    I am not sure if I missed the beginning but cleaning a simple bolt, remove paint, wire wheel and run a thread tap over it once as thread gain a very tiny amount I guess like 0.003" but many bolts have rolled threads that make them thick. A tap, cute threads and are loose. Thoughts? Thanks!
    DK, ASE master tech since 78, retired.
    (Note; I do like the "Yellow Chromate Conversion" that required a good zinc plate as the truck is a 1967 for fasteners and other items to plate. Thanks again!

  • @chrisclifford4529
    @chrisclifford4529 Před rokem

    Thanks for the informative video it sorts a lot of potential problems out. I have a question that you may be able to help with. I need to brass plate some small plastic model parts, obviously I need to paint with a conductive coating first. Do I need to copper plate, then nickel plate before I brass plate. Your advice will be appreciated. Thanks, Chris.

  • @Julia69
    @Julia69 Před 2 lety +2

    Hello. Does the acidity of the vinegar play a role? I have normals with about 5% acidity and essence with 25% acidity.

  • @TheStigma
    @TheStigma Před rokem +1

    Very good tutorial. I notice you use 5% (food grade) vinegar here. Is it better or worse to use a higher concentration? I usually get hold of 35% (meant as cleaner) where I live.

  • @MrShanksta
    @MrShanksta Před rokem +1

    Using a aeration device like the ones that make bubbles in the fish tank, but only the air tube only. This will keep the solution moving. Or using the they stir pad you mentioned? Although you didn't use it in the Nickel Plating process.

  • @ryanmiguelmariano2576
    @ryanmiguelmariano2576 Před rokem +1

    Hi, can you use those nickel plated steel strips for 18650 spot welding as nickel plating electrodes? Thank you

  • @TheFallenAngel13524
    @TheFallenAngel13524 Před 3 lety

    you can do more anodes like one on each side as long as the total surface area of the anodes is equal to or less than the surface area of the cathode.

  • @kenibnanak5554
    @kenibnanak5554 Před 3 lety

    I read on the web that common saccharin can be used as a 2nd coat brightening agent. Have you experimented with that?

  • @presidentjoethudbrandon7074

    I used a car battery and the thin strips of nickel to make the solution. I have a charger for the car battery but its one of those roll around kind and takes up a lot of room at the bench, so the battery is easier for me.
    Stripped a old charging wire to hang things from and used a paper coffee filter for the bits.
    I think in total I spent something like $15 for the vinegar and strips to make the solution.
    For the container I just used the plastic vinegar jug. Cut a slit in the bottom side and put one strip in it. Filled with hit glue to seal it.
    In the top side I made a window for a nickel strip mesh I made and lowered it in.
    The battery connections hold nicely because one can rest on the bottom of a bowl I put the jug in (just in case) and the other clips the plastic and anode up top.

  • @dezirem1231
    @dezirem1231 Před 2 lety

    Nice video !!! Some years back I nickel plated some Pennie’s do you by chance know how to reverse the effect any info will be much appreciated

  • @1580Stroker
    @1580Stroker Před 2 lety

    Thanks for nice education. Do you know what kind of material I can use that doesn't react and interfere with the solution. I want to hang down thick pieces of nickel in the bath and I guess copper-wire will interfere with the nickel solution.

  • @julram8232
    @julram8232 Před 3 lety

    Hello bit-tech, can you maby do a video on how you design the custom pc cases? I think it would be very interesting.

  • @hiseminencetheholymacdiarmada

    How would the acidic content of the vinegar effect the process?

  • @zebular
    @zebular Před rokem

    So I'm thinking of doing this for some older game consoles so as that their stock aluminum cooling blocks can use liquid metal to interface with the IHS. Will this nickel plating process work with aluminum heat sinks?

  • @anthonypla7134
    @anthonypla7134 Před 3 lety +1

    Might want to explain one reason for wearing gloves aside from messing with chemicals is to keep fingerprints from depositing on the part. My understanding is they will easily show up on the finished part. It shouldn't be an issue due to cleaning before plating but it's cheap insurance.

  • @grahamjones8890
    @grahamjones8890 Před 2 lety +3

    I am interested in electroplating a design that's been etched. Would leaving my toner on the initial part keep the nickel from adhering to the sections I desire to remain brass, or would I be better off just sanding the nickel off? My main concern with option two is that it may cause flaking.

    • @pear7777
      @pear7777 Před 2 lety +2

      No expert, just curious, what did you do? I guess etching fluid is way more aggressive than this so the toner would work? Or Nail polish, remove with acetone afterwards? I don't think you can easily remove the layer after it is plated.

  • @nipunajayashan4462
    @nipunajayashan4462 Před 2 lety

    nice. can I use this technique for my motorcycle restoration project, with vinger

  • @TinkerInTheShop
    @TinkerInTheShop Před 3 lety +2

    Did you ever get to try brighteners with this solution?

  • @benediktfrasch2812
    @benediktfrasch2812 Před 3 lety

    do you also plan on making a video on anodizing aluminium? and do you plan on anodizing the aluminium in your aquaceras project?

  • @x_Cant_01_x
    @x_Cant_01_x Před 3 lety

    I`ve been watching your AQUACERAS build, have you ever done a distro plate from copper, with an acrylic top?

  • @jasondoyle1037
    @jasondoyle1037 Před 3 lety

    Super quality presentation of a fascinating subject !
    What is the chance of heavily zinc plating the underside of a new lawn mower deck?

    • @ReadyUpGo
      @ReadyUpGo Před 3 lety

      Whoa! Did you manage that? One comment mentioned “brush plating.” I know nothing but would love to hear what you found out about that. I presume that you would need to remove all prior rust first.

  • @rkaag99
    @rkaag99 Před 2 lety +1

    Are there alternatives to the HCL acid, like acetone etc. for cleaning? I am just uncomfortable with keeping strong acid around. Thank you for the video!

    • @TeslaFactory
      @TeslaFactory Před 2 lety +2

      Acetone is good for cleaning oils, grease, and dirt, but you need an acid to remove oxidation. You could consider citric acid if you want something more gentle to activate your surface.

  • @benusarib4020
    @benusarib4020 Před 2 lety

    Very Interesteresting. !!
    In some case I need to block a certain area in one peace of metal from being plated.
    Such as motorbike exhaust pipe, how to do this efficiently?

  • @kxnfuzed2582
    @kxnfuzed2582 Před 3 lety +1

    Let's gooo.. im early.. thank you for the great content

  • @techtips3315
    @techtips3315 Před 2 lety +1

    What happens if there is paint on the surface of the metal to be plated.

  • @gopans1918
    @gopans1918 Před rokem

    I started loving Chemistry 😀

  • @kashukumar1497
    @kashukumar1497 Před 3 lety +1

    Thanks sir this video

  • @mikeconnery4652
    @mikeconnery4652 Před 3 měsíci

    Very good

  • @misticx
    @misticx Před 3 lety +3

    could you make a ring anode, that would be the same diameter as a glass beaker, would that kind of an anode prevent shadowing?

    • @archer9338
      @archer9338 Před 3 lety +1

      He could use multiple rods with 3D printed holders just like the one he uses, and connect them all with copper wire. It would allow customizable configurations for more complex parts and would be easy to do.

  • @corwinwhitehorn7759
    @corwinwhitehorn7759 Před 3 lety +2

    Wouldn't it be possible to put more anodes (around the beaker-instead of a large one) in order to mitigate shadows - with the part in the middle?

    • @apistosig4173
      @apistosig4173 Před 2 lety

      that would definiately work - keeping the solution moving would also assist.

  • @danthaman4778
    @danthaman4778 Před 2 lety

    Im trying to coat old bolts have soaked them in vinegar and removed the rust and ultrasonic cleaned them and then picked them but rust appears after would wax n grease remover or methylated spirits instead of distilled water it makes it rust

  • @simonholmqvist8017
    @simonholmqvist8017 Před 3 lety +1

    does a 6% solution of acetic acid work as well? That is a lot easier to get ahold of where I live than plain white vinager

  • @thepartsrunner5758
    @thepartsrunner5758 Před 2 lety +1

    The Scorpion tail mustache is a nice touch..

  • @anglikai9517
    @anglikai9517 Před 2 lety +1

    Hi, can we electroplating very very thick until it is like metal rod itself ?

  • @1crazypj
    @1crazypj Před 2 měsíci

    Until relatively recently, in the 1980's, a pickled black nickel was the 'darkest black' available for high end camera equipment and telescopes to prevent internal reflections.
    I think it was only within the last 10 years less reflective black has been available (as used by NASA et.al.)

  • @madscientist6843
    @madscientist6843 Před 3 lety +1

    Could you use a PC power supply for the plating process? They have 12V and 5V rail, so you could use the 12V to set up the solution and the 5V for the plating itself...

    • @sreekumarUSA
      @sreekumarUSA Před 2 lety

      Power supply is any thing that supplies power. Alex the presenter , spoke about this briefly at the introductory opening lecture. He said you could also use a phone charger also. You need to watch the segment many times to understand. Take care and be safe.

  • @rossokeefe9268
    @rossokeefe9268 Před 2 lety

    I made a batch of about 1 gallon of nickle solution but it's not working so good, seems like it won't coat the bolts..I've tried different voltage, acid bath parts..but doesn't seem to transfer to the parts,,any advice on what to check?

  • @rossokeefe9268
    @rossokeefe9268 Před 2 lety

    Would sandblasting be ideal for cleaning objects before electroplating?

  • @alwood9148
    @alwood9148 Před rokem

    i have made 2 nickle solutions seperatly Yet both have come out beetrooty colour def not green everyone has? using vinegar and salt as shown. is it perhaps volt/amps too high /low, i,m using a fully adjustable unit thanks for your input , Al

  • @jdwilliams5244
    @jdwilliams5244 Před 2 lety +1

    Where did you get your anode holder? I have looked all over for them.

  • @uksteve-passiveincomevikin3981

    Great video, very thorough.
    Would this work for silver plating?
    And how would you go about only plating part of it, for example if you had a bronze skull with horns and you only wanted to plate the horns is there something you can use to prevent the rest of it from plating?

    • @SeanBZA
      @SeanBZA Před rokem

      Just mask off parts you do not want plated. Either keep only the horns in the plating solution, or simply mask them off with say a coat of something like plasti dip or even spray paint.

  • @ABCBom4thgen
    @ABCBom4thgen Před 2 lety

    I really want to do this to the drinking water faucet I have to match my polished nickel plated kitchen faucet, but I'm super worried this isn't going to work because I am having a hard figuring out the interior of this faucet since it has a TDS display screen in the body of th faucet. Hoping someone else here has done something similar.

  • @MG-lh5tw
    @MG-lh5tw Před rokem

    hello will this work for zamak? i have a firearm wich has some parts in zamak such as trigger hammer and other small parts lately I've noticed that those parts have become very dull in color and im wondering if i can plate them in nickel to get that beautiful shine back

  • @1937Brett
    @1937Brett Před 7 měsíci

    If I wanted to protect something very well do I do copper nikle then for decorative silver or gold?

  • @christophersmith108
    @christophersmith108 Před 3 lety +6

    I imagine you could reduce the risk of shadows (especially when plating complex geometries) by using more than one anode placed around the rim of your electroplating bath, so that all parts of it are "illuminated" equally

  • @johnwetzel6200
    @johnwetzel6200 Před 2 lety +1

    Is it possible to plate tin with this same process?