- To contact me with questions or requests…please go to my website and use the “Contact Us” page. This has proven to be the best way to reach me without the risk of your email going to spam.
www.maximumguitarworks.com
We do custom template sets. Contact us if you have unique needs that no one else will do for you. Look at our website to see all the great tools, jigs, and templates that will help you to build the guitar of your dreams with precision and safety.
www.maximumguitarworks.com
Here is a special video at the request of my CZcams viewers. I was asked to show how I take a guitar top with stress cracks…and make it into a one-of-a-kind work of art. We explore many ways to approach this process…and give you all the information you need to do it yourself.
Learn more about the template systems through my past CZcams videos.
• Template Guitar Building
Here is my guitar top glue up jig video.
• Easiest Book Matched G...
I often get asked about what parts, tools, or supplies I use in my videos. Well, I have decided to create an Amazon Influencer account. It allows me to share the items I use with you…and it pays me a small commission if you purchase through my link. This is a small way you can support MGW and the content that we produce. I will look to add more products over time.
www.amazon.com/shop/maximumgu...
Maximum Guitar Works is a custom guitar shop based in Colorado USA. We are passionate about creating the highest quality instruments to meet the exact requirements of our customers. Not only do we create personalized custom guitars, we manufacture high quality production models, produce custom parts and accessories, and provide instruction for enthusiasts via our CZcams channel. Our passion for excellence is evident in everything we do!
Make sure you subscribe to the Maximum Guitar Works CZcams channel so that you don’t miss out on future videos. Feel from to post comments and/or questions below.
46 minutes!! Damn the YT metrics!! Thank you for doing proper duration videos....and the humor.
Bending over the forearm cut!! I’m am not gong to miss that! But then again, I never miss any of your videos, because I always want to start with excellence.
I really enjoyed the statement that we as humans are not perfect. Almost philosophical. Thanks for this excellent video.
Thanks Wolfgang. Sorry took me so long to reply. I fight against social media...crazy for a guy with a CZcams channel. ;-)
I wasn't sure I would like this but I really do. Much cooler than one of those epoxy table deals.
Oh and the Peanut Butter gag was brilliant
The walnut is so pretty, and the choice of the gold was spot on, going to look great - cheers from Canada
Steve that Gold foil fill looks fantastic on that Top
Thanks. I love it...need to finish that guitar and video series!
tip for coloring epoxies, add the tint to the resin, mix, then add in hardener and mix. this allows for time to mix in the color well without cutting in to the working time.
True fact...especially the resins that cure faster.
If using pearl, less is more. I've tried this many times and pearl powder works best when you use just enough to get the epoxy opaque while keeping it translucent. I think you'll be surprised how much difference it makes. Again, suggesting my friend. ✌️
Nice transformation!
That top clamping jig is magic! Thanks for showing all the different options. The final result looks great!
I know it's a year later.
With epoxies, you have to make sure when using a scale, 1:1 means weight also. Some epoxies will say 1:1 by volume. Like West system epoxies, are 1:1, and they mean one pump of resin and 1 pump of hardner. The pumps dispense the correct amounts of both resin and hardner. When mixing without the pumps and depending on the hardner, it can be 5:1, or 3:1, and will differ by weight or volume.
Also, a mistake some people make is, they add the resin, the hardner, and the color or media together,, then mix. It's very important to mix the resin and hardner thoroughly, wait a few minutes, then add the media. Epoxy doesn't dry, it cures, like you said. It's an exothermic reaction.
Try to salvage some of the cutoffs, to book match sideways, to cap the headstock to match!
Again, another good video Steve!
That is stunning!
top tip. Make extra epoxy and fill silicon, bite-size, chocolate moulds with it. Let it cure and you have guitar knobs that match the filled cracks!
Great video Steve!
So sweet brother! I'm torn...the "natural" looking ones are really nice looking, but you know I'm a sucker for the metallic stuff. (Hello "Barbie Blue Sparkle"!!!) I like 'em all. With that particular piece of wood, the gold you chose does look fantastic.
Looks great.
Excellence again!
So great as always! With your experience as a teacher, you manage to answer 1000 questions that I wouldn't have even thought of. Thanks for the detailed test. I'm really looking forward to trying this out myself now!
Hope all is well with you Thomas.
Golden Steve, lol
Great info
if you do any more tests, you should try some of that pearl powder I sent you! It does so great in epoxy and is the highest quality pearl pigment you can get! Just a suggestion. Killer video regardless.
It looks like some of the pores around the cracks are also filled with the gold epoxy. Might be cool to pore fill the whole top like that so the pores in the grain sparkle as well.
Could be cool. The options are pretty much endless.
Great video as always Steve!! I seem to remember Fodera and I believe Alembic would have some kind of black veneer between the top and back (or core) of their basses. I was wondering if that was a died wood veneer or some kind of plastic. Rockler had black died veneer last I checked so I thought that might be it. Thanks much!!
binging again
This is the video I've been waiting for!! Thanks a bunch for doing this one Steve. You and your videos are such an amazing resource for the community.
Now that the cracks are filled, and sanded back to raw wood, of course the walnut exposes its open pores again. Will you ultimately be going for a high gloss finish? If so, would you use the same epoxy for pore filling (with scrape method application), or a different product altogether (like a simtec 28x50 or aqua coat)?
Also, if this were hypothetically a maple burl top (i.e. much lighter in color), what option do you think you would have chosen?
I plan to seal with Simtec. I'm a huge fan of polyester coatings.
I like contrast for crack filling. Something that stands out...yet compliments. It is all about the personal taste of the builder...or the customer. Testing in scrap wood is the key...as the answer is often obvious.
Its a shame that the Stratocaster electronic/pick guard will cover up so much of that character. But that looks awesome.
This Strat will be the no-pickguard, rear cavity version...like our templates as seen here...
maximumguitarworks.com/products/mgw-acrylic-template-system-h-s-h-strat-rear-rout-set
what do you use on an old spruce top?
Have you yet posted the laminate top arm contour bend video? If so pls help me find it.
Also, creamy or chunky/Skippy or Jif?
czcams.com/video/qwil_YHMAaU/video.html
It is about half way through this very long video.
I tried to fill some fretless slots with pearl mica power and ca glue, and it didnt work super great.. be careful with that baking soda, it can age the wood cause chemical reaction
Yeah, epoxy seems to be much better to stuff like that.
Would it be better to put a thin layer of the ca to seal the crack andcthen proceed to fill it?
I think there are many ways to get the job done. However, it this case I don't think that CA would add any benefit. I like that the epoxy had more wood to penetrate and the texture for the epoxy to hold on to. But experiments will often prove theories.