6010 Root Pass | 3g Plate | SMAW
Vložit
- čas přidán 5. 09. 2024
- Rosendo is about to show you how to put in a root pass on a 1/2" plate in the 3g position using the SMAW welding process.
We also just launched our online store. Check it out at www.weldlife.com/ use discount code flyduck16 for 10% off total purchase.
Get yourself a custom trimmed pipeliner with aluminum fasteners and the super light weight front-flip adaptor from WeldTube.
WeldTube Online Store: www.weldlife.com/
#WeldTube #southcoastweldingacademy #Welding
WeldTube Social Media
Instagram: / weldtube
Facebook: / weldtube
TikTok: www.tiktok.com...
👇WeldTube Store👇
www.weldlife.com
2:26 You meant don't pull out a lot, only a few militer before touching the puddle, am I right?
Man this is amazing , I've been fighting this for days trying to get it right. I watched this 10 minutes later laying beads. Thank you . Great video
I’m on 3g right now. I need this like a pig needs slop
Keep at it bro . 3g roots were like kryptonite to me when i was in school.
Keep trying, don’t be bummed out if it isn’t going to well, remember every fail and learn from your mistakes and try again.
@@jeffgreer198613 Same here. Took months for me to figure it out, but once I had it, the test test where way more simple.
SAME
Same..I’m in the booth watching this rn
Thanks for this, I've been battling with the same setup on 3/8" plate in class, for the past few days. Good info that I'll try out when I go back tomorrow!
Well did you pass🤔
@@terrybrewer1622 I did! 3G and 4G
I had months
The bead on the backside says it all. Probably the easiest method to learn open root with and consistent too 😊
www.weldlife.com
WeldTube Online Store
Use discount code flyduck16 for 10% off
could we get one with a smaller plate?
Spanish!!
Can shipments be made to Spain?
I would like to buy a pipeline mask
@@diegoolivos5656 has podido comprar estas caretas para tubería, desde aquí en España es bastante difícil..
I've been having trouble with this in my welding class and I think this video gave me a better understanding.
Repetition.
Settings.
Gap.
Comfort.
They make it look easy.
Continue trying the harder positions to get better at the others.
Angle your plate to forty-five an lean away or towards you to simulate 6g.
This will make the regular four positions easier in relatively.
Just started open root in class. Thank you for showing the set up and the prep process. Much help
Got a weld test Tuesday next week for a boiler company this video came in handy
Thank you i mised some days due to an inury and was goven this as a test and u helped save me
Nice video, I got a 6010 3g on a 3/8 plate today and a bend test for midterms too. I can’t wait to get it done.
Same I have mine today😅
Don't pull out, got it ✅️
Worked on my first try. I did it at 85 Amps and worked like a charm.
85 for the root? In class they told me to do it 65-75?
I’m in spot practicing where 80 amps is a bit too hot, and 75 seems too cold my keyhole keeps closing and snuffing the arc. Drives me nuts
I’m in spot practicing where 80 amps is a bit too hot, and 75 seems too cold my keyhole keeps closing and snuffing the arc. Drives me nuts
I’m in spot practicing where 80 amps is a bit too hot, and 75 seems too cold my keyhole keeps closing and snuffing the arc. Drives me nuts
Another one for the books guys. Awesome video. Practical application.
Thanks for the video! I definitely needed this. I’ve been blowing holes in my plates in class haha. I’ll try this next time and see if i can control the heat more by not pulling out as much. I have to take my test soon.
You in school Peyden?
@@downhilldaddy9346 yup. Been in trade school for a few months now
@@Peyden what kind of welding you looking to get into?
@@downhilldaddy9346 Well I have my mig and flux certifications, but I’m working on stick now and I’ll do tig next. As far as a career goes I’m hoping I can make it on a pipeline or do some other structural work. Might try to join the local union.
@@Peyden TIG is the future. Good luck and I hope to see you in a plant sometime 🤙🏾
I will also become a Great Welder someday,. For now, I will train hard first. Don't stop until you get to the top.
With 6010 we never scare about tight gap anymore
Really great video. The film quality is amazing and the info is straight to the point. Thank you a lot for the uploads. I'm in Houston as well going to weld school and this channel has helped me alot.
Thanks for that side view. It really helps.
Niiiiiccccceeeeeeee, well explained short n simple. Keep burnin rods mate, yewwwwwwwww
I use a nickel for my landing and a quarter for my gap and it seems to work good
Still helping out fools like me. Thanks Rosendo.
Its due on the 15th and its the 13th, this is gonna be fun and not stressful
Excelente, saludos desde Chiapas México
When stitching only touch the puddle after it solidifies so go up and wait till the puddle cools down then touch it again and repeat that method, thats how i learned
Definitely took some getting used to running 6010 roots, after spending years rooting with 7016 lowHy rods.
“Do NOT pull out”. “You gotta make sure you touch your puddle”. Words to live by.
Muy educativo sus videos saludos cordiales desde panamá City 🇵🇦
Very clear and nice technique 🙏👏👏
Love your videos man. So much stuff you say I think I understand then later on I really get it and I'm like Dawm.
Great video
The 3g or has gotten me depressed af Thankyou so much
First, I was just about to comment so when are the weld tube welding gloves and products coming?? Commented too soon 🤣🤣🤣💪
Unfortunately no gloves yet it seems
Hello,
Excellent, thank you so much for your terrific technique, have a good one
Ordered the shirt and a couple stickers! Can't wait
The new helmet looks bad ass, imma but one and cut it myself for cheap 😂
Great demo !
Assalamulaikum..
Guy's I'm always watching from pangasinan, Philippines
We using E6011... Me make crazy..
By the way I'm just a student beginner
Hi bro I'm Indian 15 years ago welder
No matter what you do DO NOT pull out. Very important.
holy shit man this is perfect, thank you!
Beautiful work ❤
Excelente video y trabajo estoy soldando cañería y me ayuda mucho ,gracias
I started 3g Friday and I showed me instructor and he looked me in the eye and asked me “what the fuck is that”
BRAVO !!!!!!!!!!!!!!!!!!!!!1
Thanks Rosendo 💪🏻
I know it's hard to show on Camara but one thing this video doesn't show or express is you need to PAY ATTENTION TO THE CONSISTENCY OF THE PUDDLE, if the puddle is looking really wet you need to speed up and stack the next dime a little further apart, otherwise the puddle gets really hot and burns through or drips down. You keep doing so until the puddle stabilizes. A pointer to a stable puddle is everytime you whip out you should see your weld dry. If it stays wet when you whip back in, the puddle is too hot and it will burn through. Think of it as the reason you whip is to derive the heat away from the puddle. This is crucial in vertical welding because the puddle tends to get hotter as you go,
You made that look waaaayyy too easy bro
Maybe next video show us tig on pipe but free hand every thing
I can’t do a 3g to save my life Jesus help me
Thanks you good working ❤❤❤
I've always known this technique as "whipping" great video!
Seems like it, but when you're going horizontal, I don't think you touch your puddle
Or "jacking"
I asked around yesterday: it's basically the upwards whip and pause technique. I believe the teacher in this video repeats "touch your puddle" not because you actually do it, but to stick in your mind that your arc length should stay minimal
@@Solaniin basically it's suppose to be the same diameter as the rod your using.
Nice 👍
Cuanto amperaje usaste en el pase de raíz vertical?????
Love the tips from your videos. It's great to hear and see other people weld everybody weld differently. Side note, who makes the stinger you are using? Thanks again!
I always see the wide gaps low heat. Alot harder then people think. But a tighter gap requires more heat snd you gotta move faster so end of the day. Its preference.
That is beautiful
The sound of a p5 roasting a root off in a piece of pipe will forever be burned into my brain. Uphill down hill dont matter. Real welders turn them headohones off for that ❤
That is really nice.
very good
Thanks you via very good 👍👍
Great job man👍🏻👍🏻👍🏻
Awesome job brother! 😎👏🏻
Great stuff
What polarity is used when welding plate up hill 6010
Thanks guys for the best video on welding
Reverse
DC + is reverse polarity and Welding pipe is Down hill is DC- straight polarity
Which mean welding 6010 plate root pass is DC+ right?
Thanks for reply to my questions
DC+ is reverse polarity.
Welding pipe with a downhill progression using SMAW/Stick process will be DC+/reverse polarity. Typically you will use DC-/straight polarity with FCAW/flux core or with GTAW/Tig processes
Less gap between plates
Completa todo el.procedimiento,el pase de raiz te salio perfecto 💪😎
Nice work. More videos
My work gave me an esab 180i but I don’t weld. Is that a good beginner welder?
He'll yeah rosendo get that shit!
How much mm did grind down from the corners?
I really love your videos i really learned a lot. Im from Mexico i have a question. Is there a way to go to united states to take some courses or work there.?
What's your preferred amperage on root pass?
Very well
I see that your rod angle is almost perpendicular; I see, in other videos, welders using slight upward (20˙?) rod angle... Does that make a difference? Thanks!
My boss does almost a 80° angle and his come out amazing everytime I think it’s more preference than anything
Nice
В положении 4 G такие же движения можно использовать?
Does the same technique apply when doing it in the overhead position??
Awesome bro
Just for you brother🇮🇩
Nice weld.... Can I borrow your welding mask.. 😁
Great welds.
Buitiful brother
in the old days that technique was called whipping
North, south, whipping.
East, west, weaving.
Push? Is what I heard about driving the 60## rod into the open root, yet I don't recall if there's a name for this.
Arc length doesn't really cover it does it?
Arc length for up or down I suppose, now we have words for all three axis.
Hey rosendo is there a reason why you don’t just drag it?
The reason I don't drag is because you will run too hot and it will open up. You can drag on a tighter gap. However that's my experience with it.
Clout Lord thank you very much for the advice!!! I was just curious that’s all
@2:27. I think I would want to pullout 👶🏻👶🏼👶🏽👶🏾👶🏿😹😹😹
Deberían hacer del mismo video dos versiones en inglés y en español latino
Thanks sir
how about a "monster" coupon , 6010 root?. Please.
I have no problem running it but I can’t get one side to tie in and it’s annoying
Un vídeo en inglés y lo entendí a la perfección disculpen no entiendo ni se hablar inglés hay videos en español que no se entienden y está está súper claro a pesar que no es mi idioma jjaaja😅😂
this is so weird how he's using almost a straight angle my teachers keep telling me to not use straight angle and dont go below 80 on amps....... and no matter what i do i keep blowing through................ and straight angle caused me to blow through faster like the frustration is real.
Can y'all please show the tie in from welder's pov? I can't see anything if u showing it from the back
What kind of disc is used to clean de root pass? Any amazon links to buy them?
Tienes k poner una plaquita para entrar y otra para salir saludos bro
Do you mess with arc force/dig at all or no? I find running anything lower then 75 has me sticking like crazy. I understand all machines are different but I’m just curious
I run my roots at 60-65. You have to make sure you long arc it before you get going though or else you’ll just glob up and stick. Anything higher than 65 for me and my keyhole just gets out of control
Are you using a transformer based machine or an inverter?
@@kf8575 inverter, Miller dynasty
For the root must electrodes thinner?
I think my v groove is too narrow, not getting enough penetration because i can’t push my stick in enough
Hola buen video , saludos desde Colombia 🇨🇴, por favor crar un vídeo en español o por lo menos los subtítulos en español, gracias 👍🏻
Do a bend test and use your chipping hammer and clean off that slag on the back so can see if you are really tied in or not.
Super Azerbaycandan severek izledim