Few Things To Avoid When TIG Welding Root Pass !
Vložit
- čas přidán 10. 02. 2023
- Things To Avoid When TIG Welding Root Pass !
What is a root pass in TIG welding?
Root passes use weld filler material to close the root space between the weld faces. Follow tips regarding shielding gas, welding preparation, and weld techniques to make TIG welding your root pass successful. The video gives viewers good insights into placing excellent and solid root passes. You will get to learn about different technical paths that you can explore. With the appropriate training and practice on the operator's part, learning to place the root can become an invaluable skill!
#tigwelding #tig #tigroot
None of these videos are recorded in a fancy shop surrounded by sponsorship banners!
My videos are recorded at working sites in various locations and welding positions.
90% of my welding projects in videos are x-rayed, and if you like to see hands-on projects, welcome!
If you liked this video please give it a thumbs up, share it, subscribe, and click the bell.
It doesn’t cost you anything but massively helps my CZcams channel. Thank you.
Support this channel with 🔔 Subscribe and 👍 Like!
/ x3mtig - Věda a technologie
Best welding channel on CZcams, deserves more recognition
Thanks for your comment I appreciate that 👍
❤ I definitely agree
I have learned so much from you. I almost done with the root.
Happy to hear that brother 👍
Thank you, need more things like this to help us boilermakers
Pojasnjeno u detalje i bez bespotrebnih gluposti! Najbolji a nas!!!🇭🇷🇭🇷👏🏻
Hvala ti prijatelju 👊
@@X3MTIG znao sam da si balkanac sunce ti tvoje najbolje videe radiš i svih kritičnih detalja se dotakneš...svaka čast!
@@MrFran007 Hvala ti 👊
Great video again
Great video as always
Thanks again!
Very helpful video 🙏🙏🙏👍 sir thank you sir for video upload
Most welcome!
The most valuable content for tig welding👍🏽!!
Thank you brother 🙏😂
Merci pour cette vidéo 🙏👷🇫🇷
Hello gentlemen, In pass on,or root pass all your attentions were accurate, from the presence of tungsten and the necessary amount that should be outside of the ceramic, as well as the size of the tube gap to have good penetration to take X-rays, thank you for your accuracy.
Very helpful. Testing on 2 inch SCH 80 and will be using your advice.
Thanks buddy, and good luck 🤞
You are the best brother, thank you for all the advice’s and info!!✊🏽
You are very welcome my friend, I’m glad you like it 👍
It's very useful video to me
Thanks a lot sir
God bless you
This guy is a beast. Top side is my biggest struggle also over feeding getting too much metal on the outside of my root, but I’ll keep practicing.
Great lesson and examples, thanks
Thanks buddy, glad you liked it 👍
very good advice! i love it!
Great content
I am 18 and im learning to run tig Root and hot pass on 2” 6g position. Your Videos help me out tremendously!
Happy to hear that brother 👊👍
Can you make video about feeding the wire? I’m talking about those few techniques of feeding, what is your favourite one, and wich one is the hardest way to do it according to you.
Thanks for your suggestion bud, I can’t promise anything, but if I get some free time maybe I’ll do it.
👍🔥
Best welding Chanel on CZcams thank you
Thanks 👍
Very very good explanation to your technique. Helps me a lot. Thank you.
Very nice,good video.
I have learnt very important technique in this video I like It
Can we talk about that ruler?! Had to watch it like three times to understand what he was measuring at 3:52
9 mil
Can you do a video on when you get a little to heavy on the root an you stop because it starts to build up too much? Thanks for all your vids
Sim mestre uma bela apresentação de regulagem de amperagem distância do tungstênio e observei que ocorre uma alteração com a saída e reposição de material na onda de retorno da raíz obrigado pela orientação 🙏
Thank you my friend I appreciate that 👍
I wonder how much per hour a welder like you gets. You are my role model. Im doing city and guilds level 2 tig stainless in the uk and one day i want to weld like you
Hey bud, it al depends from your skill set, company you work for, certifications, but generally speaking, somewhere between $35 to $60 per hour!
Nice video! I notice welding to far and time on the bevels the root gets flatter.
Hey bud, great point, yes it does 👍
Beautiful
Just realized that I've been watching your vids for months without subscribing. That's fixed now though. Shame on me, and you too if you're doing the same.
Muito bom 👏👏
You are the best TIG welder/instructor on CZcams rn. You’re killing it. So many good points and your videos are crystal clear with super helpful tips. Adding so much more to my skills & technical ability everyday, you definitely help. Great community.
Thanks brother I appreciate that 👊
Good weld 🎉😊
U deserve so much more recognition than what u have we really appreciate everything u do & the knowledge u give us whatever u do don’t give up because of lack of recognition you help out alot more people than you think your channel is literally the Only channel on CZcams that breaks Everything down in detail & you actually take the time to explain everything u do step by step with a close up look I just wanted to say thank u & keep it up bro we recognize u & we’re learning from u I know I am & I’m pretty sure other people are too 💯👌
Thanks brother I appreciate that 👊
@@X3MTIG Can you tell me how you sharpen your tungstens?? U have the most sharpest cleanest tungstens I’ve ever seen
Is the ampere different on every machine? If i go 130 on the root i will burn a hole in 1 second
When you redid the root pass , what size tungsten did you change to ?
I’m always using 1/8 Tungsten
Another video with valuable info. Thanks again 🙏. Love the tip on 5:55 about the lost connection with the puddle.
Tomorow is my practice day. Feeling exhausted today, from prepearing 20+ practice pieces of tube from the scrapyard, it took whole day of inhailing rust clouds. And this video come in the right time for the inspiration i need for my practice day 😎
Thanks buddy I’m glad it would be helpful 👍
I have found that one wants enough current to “wake up” the tungsten. Up to 70-80 amps wants a 1/16 tungsten. 100+ desires a 3/32 or so.
I’ve yet to go much over a hundred, as access to 220 is difficult for me.
Best welding
Great Vid - is there one like if for stainless? I never seem to see stuff like 6" sched 40 stainless thanks!
Tops
Need help, I there some way how calibrate ampere? Bc my welding machine stuck on max when the display show 10A or more, less is still welding like a 180A
Posisi kawat tambahnya tepat di root face?
Yes
How much should be the angle or inclunination on the bottom side of the tungsten to the pipe ? When freehand and when walking the cup but especially freehand.
Kabayan!
Can u show how u do tie ins on the root
Please do this in 4 inches pipe and explain about tungsten and cap
I feel personally attacked my this video lol
lol 😂
❤❤❤
What’s the tool called that you used to check your stick out ?
Can u show us how to do a 6010 root pass
Pozdrav iz Srbije! Prenosis sustinske stvari u zavarivanju,svaka cast! Mozes li mi reci molim te koliko zatupis ivicu korena? I da li je moguce da ima toliko odstupanja u odnosima amperaza,razlike medju aparatima? Jer 130A na kempiju zvuci previse za koren i imam osecaj da bih progoreo materijal prebrzo.Oprosti na poduzem pitanju.Hvala ti na odgovoru i svako dobro zelim!
Pozdrav,
Za zatupljivanje ivice korijena sve zavisi od materijala kojeg se vari. Generalno, osobno volim, noz na crnim cijevima, a kod inoxa oko 1 do 1 1/2 mm, cisto iz prevencije “ internal undercut “ . Dali ima razlike u masinama ? Ima, naravno i meni se cak nekad desi da koristim istu masinu u elektrani i rafineriji i ima razlike u napajanju. Ovdje su uglavnom Miller i Lincoln, odlicne masine, pogotovo na diesel, ali mislim da Kempi je vise specijaliziran za Tig i sadrzi kvalitetnije komponente, tako da je sigurno razlika u amperima. Hvala ti na komentaru i svako dobro!
any tips so i don’t get suck back when I do overhead
❤
👍
Help! My root keeps coming out too flat on the inside and I don't know what I'm doing wrong!
I only can put a perfect root in on carbon at 65 or 70 amps never loose connection. If I go hotter it's constantly loosing connection and opening up the keyhole. I'm confused.. you move faster maybe?
I do move faster, but you have to work on your tungsten and filler wire inclinations…
What type of ruler is that?!?!?!?!? Our shop need one bad
Please make two runs capping e7018
The first few welds look like from me... :(
Does the rod feed have to be from the inside?!🤔🍀
For better root penetration it is always good to feed rod from inside.
@@X3MTIG thank you 🍀🇮🇪
Why is there so mutch slag on your root? I know it dosnt matter stabilitywhise,just wondering because it never happend to me or my coworkers
Tell me how to run the wire
Do you walk coming up on the left side on 6g on root?
Yes I do
Hot and covers too?
I’m testing right now ?
I’m putting an 1/8 gap and using 1/8 filler rod
Does that sound right?
My guy sounds like Zlatan
Mới tập hàn bắt đầu từ đâu
I'm in 2nd semester welding school so forgive the ignorance, but why does undercut matter on a root pass? You'll be doing a hot pass right after that will fill the undercut in anyway, yea?
I doesn’t on the outside, but on the inside matters.
@@X3MTIG oh I see, yea that makes sense. I wasn't thinking about the inside of the pipe.
😂❤and ... 90% of all errors outside in the real world is from 10 - 14 i clock ... 😅😊🎉
When welding bottom of pipe if I can't get cup to walk I like to finger the bottom and when u get puddle in bottom going pull rod up a bit and roll rod side to side it ropes that bottom part of bead right on in take your time and get right ..