Yes i'll like to do the training for the welding supervisor position because i've work in that position for about three years with many companys, plus i've been welding for more than 30 years and the most recent job as a welder on a 20 inch gas line doing down hill welding, so i really want to do the welding supervisor training for future jobs
dear sir, in question no. (27) the question about performance qualification, first should go to table qw- 451.2(a) note (1): (1) To qualify using positions 5G or 6G, a total of four bend specimens are required. then type of bend test shall be based on weld metal thickness can go to qw-451.1. thank you.
Your answers is right , Appreciated ... however the main answers is will be the 4 side bend test , if the welder qualified is 5g and 6g means they are following the one main WPS and then sure its need to follow as per the requirements side bend test QW 451.1...
sir , question 21 difference b/w gtaw and gmaw , gtaw is ok what u have explained, but in gmaw 50% argon + 50% helium u have used, both r inert gases, there should be co2.plz guide me.
![Welding engineer interview Questions [Top 90]](http://i.ytimg.com/vi/9m6cxhcfCo8/mqdefault.jpg)
![Welding engineer interview Questions [Top 90]](/img/tr.png)
![Welding engineer interview Questions Top 90 [PART 03]](http://i.ytimg.com/vi/RvaGFWRCHY4/mqdefault.jpg)
Super boss
Thanks
Q-24 HF use to avoid the tungston inculsion in weld metal and post purging to cool down tungston and save from oxidization of weld pool.
Q3 . Not included angle. It is bevel angle
Yes i'll like to do the training for the welding supervisor position because i've work in that position for about three years with many companys, plus i've been welding for more than 30 years and the most recent job as a welder on a 20 inch gas line doing down hill welding, so i really want to do the welding supervisor training for future jobs
OK...
Excellent sir thanks a lot, please keep making more video like this thanks again
Thanks for your great comment.. I always try to help my community ..
Sir for question 28 Macro & fracture test comes under Destructive Testing 🙏 Thanks for Presenting this Video for Welding Inspectors 🙏
dear sir, in question no. (27) the question about performance qualification, first should go to table qw- 451.2(a) note (1): (1) To qualify using positions 5G or 6G, a total of four bend specimens are required. then type
of bend test shall be based on weld metal thickness can go to qw-451.1.
thank you.
Your answers is right , Appreciated ... however the main answers is will be the 4 side bend test , if the welder qualified is 5g and 6g means they are following the one main WPS and then sure its need to follow as per the requirements side bend test QW 451.1...
Question No 28 ...Here the question should be changed to destructive test..
Excellent sir
Thanks for your compliment
Thanks you very much sir,❤️
Welcome
Welding position is essential variable?
sir , question 21 difference b/w gtaw and gmaw , gtaw is ok what u have explained, but in gmaw 50% argon + 50% helium u have used, both r inert gases, there should be co2.plz guide me.
Sir is any parameters of voltage and current as per thickness required to maintain? If yes then in which section of AMSE maintained?
What is the thump rule?
What is mean?
Sir welding inspection ka interview hindi mai nhi hota hai muje english bahut kam aati hai
i will try to make one video in hindi
@@WeldingNDTInspection sir ndt level 2 karne ke baad minimum and maximum salary kitni hoti hai